Test report No. 2501-02 – SIA AJV Office

1. Test object:
   • Mounting plates with sizes 50 x 80 mm and 80 x 120 mm.
   • Various thicknesses tested.
2. Test methods:
   • Compression test according to the client's methodology.
   • Testing carried out at the LU MMI Materials Testing Laboratory from January 24 to 28, 2025.
3. Testing equipment:
   • Load and deformation were measured with the ZwickRoell Z100 TEW electromechanical material testing equipment.
   • Temperature was controlled with the ZwickRoell BTE-TC 12.00 temperature chamber.
   • Calibration took place on January 24, 2023.
4. Testing conditions:
   • Three temperature regimes: -20 °C, 20 °C, and 40 °C.
   • Each sample was conditioned for 10 minutes before testing.
5. Sample groups and sizes:
   • 150 samples were tested, marked with different labels according to size and temperature (e.g., S-2-C, L-3-H, etc.).
6. Results:
   • Deformation was measured at 35 kN and 100 kN loads.
   • The average deformation values in various sample groups ranged from 0.067 mm to 3.343 mm, depending on the load and temperature.
7. Notes:
   • Samples were carefully prepared to avoid erroneous deformation values by removing protrusions from the top plates.
8. Conclusions:
   • The test results are representative only for the tested materials.
   • The reproduction of the report is prohibited without full permission.